POLYETHYLENEIMINE

POLYETHYLENEIMINE
CAS NUMBER:9002-98-6

 

 


SYNONYMS: PEI; POLYETHYLENEIMINE; polyethyleneimine; Polyethyleneimine; polyethyleneımıne; polyethyleneımın; polyethylene; imin; imine; ımın; ımıne; polietyhleneimin; poliethyleneımıne; poliethyleneimin; poliethyleneimine; polietilenimin; polietilenimine; polietilenımın; polietylenimine; polietylenımıne; polietylenimin; Polyethyleneimine, branched, M.W. 600, 99%; Polyethyleneimine, branched, M.W. 1,800, 99%; Polyethyleneimine, branched, M.W. 70,000, 30% w/v aq. soln.; Polyethyleneimine, branched, M.W. 50,000 - 100,000, 30% w/w aq. soln.; Polyethylenimine, Branched, Mw 750,000, 33% w/v aq. soln. (bPEI 750000 33% soln.); polyethyleneimine, branched, M.W. 1,200, 99%; PEI-7;PEI-10;PEI-15;PEI-30;PEI-35;PEI-45;PEI-250;PEI-275;PEI-700;PEI-14M; Poly(ethyleneimine) solution ~50% in H; Polyethyleneimine, branched, M.W. 10,000, 99%; Poly(ethyleneimine) solution analytical standard, 50% (w/v) in H; Ethanolamine; Polyethylenimine; 2-AMINOETHYL HYDROGEN SULFATE; Ethyleneimine; POLYETHYLENEIMINE, BRANCHED;Aziridine,homopolymer;Ethyleneimine,homopolymer;polyethylenimine(10,000); polyethylenimine(20,000);polyethylenimine(35,000);polyethylenimine(40,000);Ethylene imine polymer solution; EPOMIN; epomin; Polymin P; polimin P; poliethylene imine; poliethyleneimine; POLIETHYLENEIMINE; polietilen; POLİETİLENİMİN; POLİ ETİLEN İMİN; POLİ ETİLENİMİNE; polietilen imin; polietilenimine; politilennimin; polyethylenimine; POLYETHYLENEIMINE; POLYETHYLENEIMIN; POLİETİLEN İMİN

 

Polyethyleneimine is clear viscous liquid.

Work described by Meyers and Royer¹ in 1977 has led to the commercial availability of a variety of products based upon polyethylenimine (PEI) technology. These include a variety of precious metal PEI catalysts* that are clearly advantageous over conventional supported and unsupported catalysts in areas such as benzyltype protectinggroup cleavage, reductions of aromatic-nitro groups and peptide syntheses.

COMPOSITION
The monomer is easy to describe. It consists of a three-membered ring. Two corners of the molecule consist of -CH2- linkages. The third corner is a secondary amine group, =NH. In the presence of a catalyst this monomer is converted into a highly branched polymer with about 25% primary amine groups, 50% secondary amine groups, and 25% tertiary amine groups. This product is sometimes called "pure polyethyleneimine" in order to differentiate it from certain copolymers of ethyleneimine and acrylamide. The latter mixture is copolymerized to produce so-called "modified PEI," that has a molecular mass up to about 2 million grams per mole. Each of these types of products is delivered to the mill in the form of viscous solutions. Solids contents are the range of about 10 to 50%, depending on molecular mass.


Melting point:59-60°C
Boiling point:250 °C(lit.)
Density 1.030 g/mL at 25 °C
refractive index n20/D 1.5290
Flash point:>230 °F
storage temp. 2-8°C
form Liquid
color Pale yellow
Water Solubility Soluble in water.
Sensitive Hygroscopic

SOLUBILITY

Liquid Solubility Soluble in toluene, methanol, ethanol, chloroform and xylene. Insoluble in water, alcohol, benzene, ethyl ether and acetone.

FUNCTION
Pure PEI is very effective for neutralization of excess anionic colloidal charge, especially under acidic and neutral pH conditions. Modified PEI copolymers having relatively high molecular mass can be effective for drainage and pitch control.

Branched Polyethylenimine, Mw 2,000,000, 25% w/v aq. soln. (bPEI 2000000 25% soln.) is highly branched polyamine with high cationic charge density. bPEI 2000000 contains primary, secondary, and tertiary amine groups with pH 8.

Industrially, branched polyethylenimine (bPEI) have extensive applications as an auxiliary agent intensifying manufacturing processes and improving quality of the final products. Branched Polyethylenimine are widely used in: paper-making, water treatment, detergents, adhesives, and cosmetics. In research, Branched Polyethylenimine are extensively investigated as non-viral vector carriers.

Crosslinked derivatives of PEI are potential chromatographic supports and ion exchangers because of their binding capacity for a wide range of metals. Applications would likely include purification of mercurycontaminated waste water and precious-metal reclamation.

PEI immobilized on a rigid inorganic matrix of high porosity is ideal for use in columns or in suspension (without magnetic stirrers). It binds polyanions, such as nucleic acids, very strongly. Suggested applications include chromatography of proteins, nucleotides and nucleic acids. It also effectively binds metal ions such as Ni2+, Pd2+, Pt2+, Co2+ and Cu2+.

Supported on an inorganic powder, this resin is suitable for use in suspension with magnetic stirrers and is usually conducive to rapid removal by filtration or centrifugation.
The PEI powder has been used in the chromatographic resolution of adenosine, AMP, ADP and ATP with a sodium chloride gradient. All components were recovered in 100% yield, unchanged, as shown by TLC and highvoltage electrophoresis.

These resins show a greater degree of hydrophobic character because of pendant benzyl groups, and strongly bind anions with polar components.

ADVANTAGES

The highest cation density among other existing materials.
Very high reactivity.
Water solubility.

STRAGETIES FOR USE
The branched nature and exceptionally high charge of pure PEI make it an excellent choice for treatment of highly anionic furnish, furnish that has a high electrical conductivity, or thick-stock furnish. The branched structure is believed to provide some resistance to penetration of the molecule into very small slit-like pores in the fiber cell wall. The colloidal charge, filtrate turbidity, and drainage characteristics of the furnish should be monitored when selecting or optimizing PEI dosage. The modified PEI copolymer is usually added relatively late in the thin-stock cycle in order to achieve a significant boost in first-pass retention and the rate of drainage. Neither additive is expected to be cost-effective in furnish having pH values in excess of about 8, since the amine groups rapidly lose their charged character above that point. Likewise, strongly varying pH values are expected to cause variations in the performance of PEI products.

APPLICATIONS

Polyethyleneimine, branched, M.W. 10,000 acts as an auxiliary agent. It is used in paper-making, water treatment, detergents, adhesives and cosmetics. It is investigated as non-viral vector carriers in research.

Anchor coating agents, Flocculants, Cation agent, Adhesive modifier

Used as a polyelectrolyte multilayer on charged surfaces to provide a biocompatible coating on surfaces.Detergents, adhesives, water treatment, printing inks, dyes, cosmetics, and paper industry, adhesion promoter, lamination primer, fixative agent, flocculant, cationic dispersant, stability enhancer, surface activator, chelating agent, scavenger for aldehydes and oxides.

 

 

 

 

 

 


Polietilenimin, berrak viskoz sıvıdır.

Meyers ve Royer tarafından 1977'de tanımlanan iş, polietilenimin (PEI) teknolojisine dayanan çeşitli ürünlerin ticari olarak bulunmasına neden olmuştur. Bunlar, benzil-tipi koruma grubu yarılması, aromatik-nitro gruplarının indirgenmesi ve peptid sentezleri gibi alanlarda geleneksel olarak desteklenmiş ve desteklenmeyen katalizörlere kıyasla açıkça avantajlı çeşitli değerli metal PEI katalizörleri * içerir.

BİLEŞTİRME, KOMPOZİSYON
Monomerin tanımlanması kolaydır. Üçlü bir halkadan oluşur. Molekülün iki köşesi -CH2- bağlarından oluşur. Üçüncü köşe, ikincil bir amin grubu, = NH'dir. Bir katalizörün mevcudiyetinde bu monomer, yaklaşık% 25 birincil amin grupları,% 50 ikincil amin grupları ve% 25 üçüncül amin grupları ile çok dallanmış bir polimer haline dönüştürülür. Bu ürün bazen etilenimin ve akrilamidin bazı kopolimerleri arasından ayırt etmek için bazen "saf polietilenimin" olarak adlandırılır. Son karışım, mol başına yaklaşık 2 milyon gram molekül kütlesine sahip olan "modifiye PEI" üretmek üzere kopolimerleştirilir. Bu tür ürünlerin her biri viskoz çözeltiler şeklinde değirmene teslim edilir. Katı maddeler moleküler kütleye bağlı olarak yaklaşık% 10 ila 50 aralığındadır.

Erime noktası: 59-60 ° C
Kaynama noktası: 250 ° C (aydınlık)
Yoğunluk 1.030 g / mL, 25 ° C'de
kırılma indisi n20 / D 1.5290
Parlama noktası:> 230 ° F
saklama derecesi. 2-8 ° C
Sıvı Form
soluk sarı
Suda Çözünürlük Suda özünebilir.
Hassas Higroskopik

ÇÖZÜNÜRLÜK

Sıvı Çözünürlüğü Tolüen, metanol, etanol, kloroform ve ksilen içinde çözülür. Su, alkol, benzen, etil eter ve asetonda çözünmez.

İŞLEVİ
Saf PEI, özellikle asidik ve nötr pH koşullarında aşırı anyonik koloidal yükün nötrleştirilmesi için çok etkilidir. Nispeten yüksek moleküler kütleye sahip değiştirilmiş PEI kopolimeri, drenaj ve zift kontrolü için etkili olabilir.

Dallanmış Polietilenimin, Mw 2,000,000, ağırlık / ağırlık% 25 aq. çöz. (bPEI 2000000% 25 solüsyon) yüksek katyonik yük yoğunluğuna sahip yüksek oranda dallı poliamindir. bPEI 2000000, pH 8 olan birincil, ikincil ve üçüncül amin gruplarını içerir.

Endüstride dallı polietilenimin (bPEI), imalat süreçlerini yoğunlaştıran ve nihai ürünlerin kalitesini arttıran yardımcı bir ajan olarak geniş uygulamalara sahiptir. Dallanmış Polietilenimin, kağıt yapımı, su arıtımı, deterjanlar, yapıştırıcılar ve kozmetik alanlarında yaygın olarak kullanılmaktadır. Araştırmada, Dallı Polietilenimin, yaygın olarak viral olmayan vektör taşıyıcıları olarak araştırılmıştır.

PEI'nin çapraz bağlı türevleri, geniş bir metal aralığı için bağlanma kapasiteleri nedeniyle potansiyel kromatografik destekler ve iyon değiştiricilerdir. Başvurular büyük olasılıkla cıva kirli kontamine atık suyun arıtılması ve kıymetli madenlerin ıslahı içerecektir.

Yüksek gözenekliliğe sahip katı bir inorganik matriste hareketsizleştirilmiş olan PEI, kolonlarda veya süspansiyonda (manyetik karıştırıcılar olmadan) kullanım için idealdir. Nükleik asitler gibi polianyonları çok güçlü bir şekilde bağlar. Önerilen uygulamalar protein, nükleotid ve nükleik asitlerin kromatografisini içerir. Aynı zamanda Ni2 +, Pd2 +, Pt2 +, Co2 + ve Cu2 + gibi metal iyonlarını etkili bir şekilde bağlar.

İnorganik bir toz üzerinde desteklenen bu reçine, manyetik karıştırıcılarla süspansiyon halinde kullanıma uygundur ve genellikle filtrasyon veya santrifüjle hızlı bir şekilde uzaklaştırılmaya elverişlidir.
PEI tozu, adenosin, AMP, ADP ve ATP'nin bir sodyum klorür gradyanı ile kromatografik çözünürlüğünde kullanılmıştır. Tüm bileşenler, TLC ve yüksek voltaj elektroforeziyle gösterildiği gibi, değişmeden% 100 verimle elde edildi.

Bu reçineler sarkık benzil grupları nedeniyle daha fazla hidrofobik karakter gösterirler ve anyonları kutupsal bileşenlerle kuvvetle bağlarlar.

AVANTAJLARI

Mevcut diğer malzemeler arasında en yüksek katyon yoğunluğu.
Çok yüksek reaktivite.
Su çözünürlüğü.

KULLANIM STRATEJİLERİ
Dallanmış tabiat ve saf PEI son derece yüksek şarjı, yüksek bir elektrik iletkenliğine sahip yüksek oranda anyonik bir döşeme, veya kalın stoklu mobilyanın tedavisi için mükemmel bir seçimdir. Dallı yapının, molekülün lif hücresi duvarındaki çok küçük yarık benzeri deliklere nüfuz etmesine bir miktar direnç sağladığı düşünülmektedir. PEI dozajını seçerken veya optimize ederken, ambalajın koloidal yükü, filtrat bulanıklığı ve drenaj özellikleri izlenmelidir. Modifiye edilmiş PEI kopolimeri, ilk geçiş tutma oranındaki ve drenaj oranındaki belirgin artışı sağlamak için genellikle ince stok çevriminde nispeten geç eklenir. Ne katkı maddesinin, yaklaşık 8'den fazla pH değerine sahip olması, bu amin gruplarının hızla yüklü karakterini bu noktadan daha fazla kaybetmesinden dolayı, maliyet açısından etkili olması beklenir. Aynı şekilde, kuvvetle değişen pH değerlerinden PEI ürünlerinin performansında değişikliklere neden olması beklenir.

UYGULAMALAR

Polietilenimin, dallanmış, M.W. 10,000, bir yardımcı madde olarak işlev görür. Kağıt yapımında, su arıtımında, deterjanlarda, yapışkanlarda ve kozmetiklerde kullanılır. Araştırmalarda viral olmayan vektör taşıyıcıları olarak araştırılmıştır.

Çapa kaplama maddeleri, Pıhtılaşma önleyiciler, Katyon ajanı, Yapıştırıcı değiştirici

Yüzeylerde biyolojik olarak uyumlu bir kaplama sağlamak için yüklü yüzeylerde polielektrolit çok tabakalı olarak kullanılır. Deterjanlar, yapışkanlar, su arıtımı, baskı mürekkepleri, boyalar, kozmetik ve kağıt endüstrisi, yapışma arttırıcı, laminasyon astarı, fiksatif madde, pıhlaştırıcı, katyonik dispersan, stabilite arttırıcı , yüzey aktifleştirici, kenetleme maddesi, aldehitler ve oksitler için süpürücü.