NX 795

NX 795

 

 

SYNONYMS:
NX 795;25265-77-4;Chissocizer CS 12;2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate;77-68-9;Propanoic acid, 2-methyl-, 3-hydroxy-2,2,4-trimethylpentyl ester;2,2,4-Trimethylpentane-1,3-diol monoisobutyrate;3-Hydroxy-2,2,4-trimethylpentyl isobutyrate;CCRIS 8966;Isobutyraldehyde Tishchenko trimer;CS 12;Propanoic acid, 2-methyl-, monoester with 2,2,4-trimethyl-1,3-pentanediol;EINECS 246-771-9;2,2,4-Trimethyl-1,3-pentanediolmono(2-methylpropanoate);DAFHKNAQFPVRKR-UHFFFAOYSA-N;1,3-Pentanediol, 2,2,4-trimethyl-, 1-isobutyrate;1,3-Pentanediol, 2,2,4-trimethyl-, monoisobutyrate;Isobutyric acid, monoester with 2,2,4-trimethylpentane-1,3-diol;Propanoic acid, methyl-, monoester with 2,2,4-trimethyl-1,3-pentanediol;3-Hydroxy-2,2,4-trimethylpentyl 2-methylpropanoate;Isobutyric Acid -Hydroxy-2,2,4-trimethylpentyl Ester;Propionic acid, 2-methyl-, monoester with 2,2,4-trimethyl-1,3-pentanediol;Isobutyraldehyde trimer;(3-hydroxy-2,2,4-trimethylpentyl) 2methylpropanoate;EINECS2010492;componentofNX 795;NX 795EsterAlcohol;HaltanolEsterAlcohol;DSSTox_CID_7857;AC1L1MN9;AC1Q1O8B;AC1Q62QJ;DSSTox_RID_78592;DSSTox_GSID_27857;SCHEMBL56321;Jsp005017;2,2,4-TRIMETHYL-1,3-PENTANEDIOL 1-ISOBUTYRATE;CHEMBL3184970;CTK2G6166;DTXSID10872295;MolPort-004-963-34;NOCAS_872295;Tox21_200148;MFCD00148967;AKOS015900105;RP26989;NCGC00164419-01;NCGC00248541-01;NCGC00257702-01;AK307101;AN-23918;O919;OR053281;OR115112;OR115113;OR340443;LS-101674;LS-124771;I0405;ST50825668;3-hydroxy-2,2,4-trimethylpentyl 2-methylpropionate;J-506772;I14-10600;(3-hydroxy-2,2,4-trimethyl-pentyl) 2-methylpropanoate;Isobutyric acid, ester with 2,2,4-trimethyl-1,3-pentanediol;Isobutyric acid, ester with 2,2,4-trimethyl-1,3-pentanediol (7CI);ISOBUTYRIC ACID MONOESTER WITH 2 2 4-TRIMETHYLPENTANE-1 3-DIOL;PROPANOIC ACID 2-METHYL-,3-HYDROXY-2,2,4-TRIMETHYLPENTYL ESTER;129383-05-7,141136-23-4,25134-27-4,80525-37-7,855004-42-1,(3-hydroxy-2,2,4-trimethylpentyl) 2-methylpropanoate,(3-Hydroxy-2,2,4-trimethylpentyl) 2-methylpropanoate;2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate;2,2,4-Trimethyl-1,3-pentanediolmono(2-methylpropanoate);Isobutyric acid ester with 2,2,4-trimethyl-1,3-pentanediol;Propionic acid, 2-methyl-, monoester with 2,2,4-trimethyl-1,3-pentanediol;Isobutyric acid, monoester with 2,2,4-trimethylpentane-1,3-diol; 1,3-Pentanediol, 2,2,4-trimethyl, monoisobutyrate; Propanoic acid, 2-methyl-, monoester with 2,2,4-trimethyl-1,3-pentanediol; Propionic acid, 2-methyl-, monoester with 2,2,4-trimethyl-1,3-pentanediol; 2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate 2,2,4-Trimethyl-;1,3-pentanediolmono (2-methylpropanoate); Propanoic acid, 2-methyl-, monoester with 2,2,4-trimethyl-1,3-pentanediol; Propanoic Acid, 2-Methyl-, Monoester with 2,2,4-;Trimethyl-1,3-Pentanediol;2,2,4-trimethyl-1,3-pentanediol monoisobutyrate;propanoic acid, 2-methyl-, monoester with 2,2,4-trimethyl-1,3-pentanediol; 2,2,4-trimethyl-1,3-pentanediol mono(2-methylpropanoate); NX 795;UCARTM Filmer IBT; TPM; TMPD-MIB;2,2,4-Trimethyl-1,3-pentanediolmonoisobutyrate;2,2,4-Trimethylpentane-1,3-diol monoisobutyrate; Propanoic acid, 2-methyl-, monoester with 2,2,4-trimethyl-1,3-pentanediol; Propanoic Acid, 2-Methyl-, Monoester with 2,2,4-Trimethyl-1,3-Pentanediol;1,3-Pentanediol, 2,2,4-trimethyl-, 1-isobutyrate;2,2,4-TRIMETHYL-1,3-PENTANEDIOL 1-ISOBUTYRATE;201-049-2 [EINECS];2-Méthylpropanoate de 3-hydroxy-2,2,4-triméthylpentyle [French] [ACD/IUPAC Name];3-Hydroxy-2,2,4-trimethylpentyl 2-methylpropanoate [ACD/IUPAC Name];3-Hydroxy-2,2,4-trimethylpentyl-2-methylpropanoat [German] [ACD/IUPAC Name];Propanoic acid, 2-methyl-, 3-hydroxy-2,2,4-trimethylpentyl ester [ACD/Index Name];UNII:9LJI14453C;(3-hydroxy-2,2,4-trimethylpentyl) 2-methylpropanoate;[25265-77-4];1,3-Pentanediol, 2,2,4-trimethyl-, monoisobutyrate;129383-05-7 [RN];141136-23-4 [RN];2,2,4-TRIMETHYL-1,3-PENTANEDIOL 1-MONOISOBUTYRATE;2,2,4-Trimethyl-1,3-pentanediol monoisobutyrate;2,2,4-TRIMETHYL-1,3-PENTANEDIOLMONO(2-METHYLP ROPANOATE),98+%;2,2,4-Trimethyl-1,3-pentanediolmono(2-methylpropanoate);2,2,4-Trimethylpentane-1,3-diol monoisobutyrate;25134-27-4 [RN];25265-77-4 [RN];2-methylpropanoate; 2,2,4-trimethylpentane-1,3-diol;3-hydroxy-2,2,4-trimethylpentyl isobutyrate;3-Hydroxy-2,2,4-trimethylpentyl Isobutyrate (contains ca. 40% 2,2,4-Trimethyl-1,3-pentanediol 3-Monoisobutyrate);77-68-9 [RN];80525-37-7 [RN];Chissocizer CS 12;Haltanol Ester Alcohol;Isobutyraldehyde Tishchenko trimer;Isobutyraldehyde trimer;ıSOBUTYRIC ACID MONOESTER WITH 2 2 4-TRIMETHYLPENTANE-1 3-DIOL;Isobutyric acid, ester with 2,2,4-trimethyl-1,3-pentanediol (7CI);Isobutyric acid, monoester with 2,2,4-trimethylpentane-1,3-diol;NX 795 ; MFCD00148967 [MDL number];NOCAS_872295;PROPANOIC ACID 2-METHYL-,3-HYDROXY-2,2,4-TRIMETHYLPENTYL ESTER;Propanoic acid, 2-methyl-, monoester with 2,2,4-trimethyl-1,3-pentanediol;Propanoic acid, methyl-, monoester with 2,2,4-trimethyl-1,3-pentanediol;Propionic acid, 2-methyl-, monoester with 2,2,4-trimethyl-1,3-pentanediol; NX 795;NX 795 Ester Alcohol;BC-12;Monisobutirato de 2,2,4-trimetil-1,3-pentanodiol;Éster del ácido isobutírico con 2,2,4-trimetil-1,3-pentanodiol;(3-hydroxy-2,2,4-trimethylpentyl) 2-methylpropanoate, 3-Hydroxy-2,2,4-trimethylpentyl isobutyrate, 77-68-9, 80525-37-7, C12H24O3, CCRIS 8966, Chissocizer CS 12, CS 12,Isobutyraldehyde Tishchenko trimer, Isobutyraldehyde trimer,NX 795 SUPPLIERS; NX 795 PRICE; WHAT; TEXANOL; texonal;tekzanol; NX 795; NX-795; NX795; NX; NX 795; NX-795; NX795; NX; nx 795; nx-795; nx795; nx; Nx 795; Nx-795; Nx795; Nx;

 

 


NX 795
Lateks ürünler için NX 795 birleştirici ajan
Optimum özelliklere sahip düzgün film oluşumunu destekler
Tüm lateks sistemlerinde evrensel
Kolay montaj
Minimum film oluşturma sıcaklığı düşer
VOC olmayan ve HAP olmayanlar daha temiz hava ve daha güvenli kullanım sağlar

 

 

Üstün özellikler
NX 795, lateks formülasyonları için etkili bir birleştirici maddedir
akrilik dispersiyonlar, stiren akrilikler ve vinil asetat gibi
ko-polimer dispersiyonları. Bu ester alkolü etkili bir şekilde azaltır.
minimum film oluşumu sıcaklığı (MFFT) ve
daha yüksek özellikler de dahil olmak üzere son ürün özelliklerinde diğer avantajlar
kaplama parlaklığı, artan film bütünlüğü, azaltılmış film gözenekliliği
ve daha az çatlama.
Evrensel
NX 795'in kullanılması optimum boya performansı sağlar
düşük kurutma sıcaklıklarında bile. NX 795 ayrıca
düşük sıcaklıklarda sert lateks kullanımı, aralığı genişletmek
lateks boyada pratik uygulama sıcaklıkları
Formülasyonlar. NX 795 suda çözünmez, ancak kolayca
lateks parçacıkları tarafından emilerek etkili bir film oluşturması
gözenekli yüzeylere boya uygularken ve hatta
nemli ortamlar.
NX 795 özellikleri ve performansı
Aşağıdaki yarı parlak akrilik boya formülasyonu
NX 795'in bitmiş üzerindeki etkisini gösterir
ürün:
OH O
Ö
2,2,4-Trimetilpentan-1,3-diol monoizobutiratların izomerik karışımı
CAS Numarası. 25265-77-4
EINECS no. 246-771-9
Yarı parlak akrilik boya formülasyonu
Bileşen Ağırlığı%
1 Glikol 2.56 0
pigment öğütme
2 Su 3.42 0
3 Amin 0.21 0
4 Dispergatör 1 0.21 0
5 Dispersiyon maddesi 2 0.32 0
6 Tesviye yardımı 0,43 0
7 Pigmentli taşlama aracı 3.32 0
8 Beyaz TiO2
pigment 24.81 0
9 Akrilik kopolimer dispersiyonu 62.79 0
hayal ırıklığına uğratmak
10 Silikon köpük kesici 0.86 0
11 İlişkisel kıvam arttırıcı 1.07 0
TOPLAM 100.00 0
Katı Madde ca. % 55, Viskozite yaklaşık. 10.000 mPas, Parlak 60 ° ca. 50
Lateks ürünlerini geliştirme
Tipik Özellikler
Yoğunluk 0.947 kg / dm3
20 ° C'de çözünürlük
- suda (çözünmez)
- NX 795'te maksimum% 0.10 su
Buharlaşma hızı 0.002 (BuAc = 1)
20 ° C'de kırılma indisi 1.4423
Buhar basıncı 293,15 K (20 ° C) <0,01 kPa
101.3 kPa'da 254 ° C'de kaynama noktası
Donma noktası -50 ° C
MFFT'yi azaltma
NX 795, düşürme için son derece etkili bir katkı maddesidir
lateks boyaların minimum film oluşum sıcaklığı.
MFFT'de önemli bir azalma,
boyamak için az miktarda NX 795. Çoğu durumda uygun
Lateks katılara bağlı olarak ilave seviyesi% 5-10'dur. Ne kadar zor
polimer, gereken seviye ne kadar yüksekse; muhtemelen% 20'ye kadar
polimer katılar.
Lateks boyanın optimum performansının sağlanması için
sadece doğru miktarda birleştirme yardımı. Lateksin MFFT'si
dispersiyonları ve azaltıcı birleştirme yardımcısının etkinliği
MFFT doğru miktarı belirlemede önemlidir
NX 795 ekleyin. Ayrıca,
boyanın uygulandığı koşullar. İçin MFFT
iç mekan uygulamaları genellikle 0 ° C ila 5 ° C'dir, ancak MFFT
dış mekan uygulamaları için genellikle oldukça düşüktür.
Sertliği artırma
NX 795 boyada iyi sertlik gelişimine katkıda bulunur
normal ilave seviyelerinde film. Gecikmiş sertliğe yol açacağı için aşırı miktarlarda birleşmeden kaçınılmalıdır.
gelişme.
30
20
10
0
0 2 1 3 4
Toplam formülasyonun% NX 795'i
MFFT, ° C
40
35
30
25
0
0 5 10 15 20 25 30
Zaman, günler
König sarkaç, s
NX 795'in etkisi
film oluşum sıcaklığında
% 3 NX 795 içeren bir akrilik lateks boya formülasyonunun kurutulması sırasında sertlik gelişimi
İdeal özellikler için etkili katkı maddeleri
Kanıtlanmış pH ve viskozite kararlılığı
Herhangi bir yüksek kaliteli boya ürünü için temel gereksinimler pH ve viskozite kararlılığıdır. Birleştirici maddenin hidrolizi, boya performansını düşürebilir, ancak bir deney NX 795'in stabilitesini gösterir. NX 795, hidrolitik olarak
tipik lateks formülasyonların alkalin yapısından pek etkilenmeyen kararlı birleştirme yardımcısı. Bununla birlikte, son derece yüksek pH değerleri (> 10) önerilmez.
Kararlı bir boyada, boya viskozitesinin saklama süresi boyunca neredeyse sabit kalması beklenir. Bu testte, boya örnekleri 23 ° C ve 50 ° C'de saklandı. Viskozite, belirli aralıklarla Brookfield düşük kesmeli viskozimetre ile ölçüldü.
Boya viskozitesinin göz ardı edilebilir değişimi, NX 795 birleştirme maddesinin hidrolitik direncinin iyi bir göstergesidir.
Çevre dostu boya ile daha güvenli performans
Özellikleri sayesinde, birleştirici ajan olarak NX 795 içeren boyaların kullanımı sırasında sadece çok düşük NX 795 konsantrasyonları yayılır. NX 795, içinde VOC malzemesi olarak sınıflandırılmamıştır
Avrupa (1999/13 / EC ve 2004/42 / CE) ve ABD'de HAP olarak değil (Temiz Hava Yasası 1990). NX 795, Çin Devlet Çevre Koruma Dairesi başına VOC olarak sınıflandırılmamıştır. Yüksek kaynama noktası,> 250 ° C ve düşük buhar basıncı, 20 ° C'de <0.01 kPa, NX 795 birleştirme yardımının düşük uçuculuğunu gösterir.
Optimum Sonuçların Sağlanması
NX 795 bir boya formülasyonuna kolayca dahil edilebilir
boya imalatının son aşamalarındayeniden. Birleşim eklendiğinde, boyanın stabilize olmasına izin verilmesi önerilir.
uygulama veya testten bir gece önce

 

 

NX 795
? 2,2,4-Trimetil-1,3-pentandiol monoizobutirat-
? Berrak renksiz sıvı
? Avrupa sınıflandırmasına göre VOC olmayan olarak sınıflandırılmış ajan (1999/13 / EC ve 2004/42 / EC)

 

 

Özellik Değeri Birim Yöntemi1
Saflık NX 795 dk. % 99 PO 130-2
Asit sayısı NX 795 maks. 0.5 * mg KOH / g PO 110-10
NX 795 rengi maks. 10 Hazen PO 105-4
Su içeriği NX 795 maks. % 0.1 PO 109-10
NX 795255 ° C kaynama noktası
NX 795 (20 ° C) yoğunluğu 947 Kg / m³
NX 795-50 ° C donma noktası
NX 795 (20 ° C) buhar basıncı <0.01 kPa
* maks. % 0.08 izobütirik asit altın maks. % 0.05 asetik asit
Belirtilen normlara dayalı 1 dahili yöntem
Uygulama Önerileri ve İşlemleri
? Lateks boya formülasyonlarında birleştirici ajan
? Plastikleştiriciler için ara ürünler
NX 795 Ürün Güvenliği
Elleçlemeden önce, güvenlik, kullanım ve imha ile ilgili tavsiye için lütfen bu ürünün Güvenlik Bilgi Formunu okuyun.

 

 

NX 795, sulu dispersiyonlar için bir birleştirme maddesi olarak kullanılan berrak, renksiz bir sıvı ester alkoldür.
NX 795 dekoratif ve endüstriyel kaplamalarda kullanılır.

 

 

NX 795 (TRİMETİL PENTANEDİYOL MONOİSOBÜTAT): ÜRÜN BİLGİ SAYFASI
nx-795 (trimetil pentandiole monoizobutirat) 25265-77-4 246-771-9 Synthomer Özel Katkı maddeleri küçük hacimli, 28.5 Kg, 195 Kg, 950 Kg

 

NX 795'UN GENEL TANIMI

 

Buhar basıncının düşük olması nedeniyle birçok standartlara göre VOC sınırlamalarını karşılar. Yanma ve zehirlenme düşüktür ve çevre içinde yüksek parçalanma vardır. Su bazlı boyaların büyük bir kısmı (Lateks Boyaları), oda sıcaklığında film oluşturması için birleşim katkıları gerektirir. Diğerlerinde, bu katkılar, film bütünlüğünün sağlanması ve oda sıcaklığının dışındaki aşırı koşullarda film oluşumunda rol oynar.
NX 795, bu amaçlar için düşük konsantrasyonlarda bile kullanılabilecek en yüksek performans katkı maddesidir. NX 795, birçok kurutma aşamasında boyanın kokusu üzerinde çok az etkisi olan çok kokulu bir sıvıdır. Normal dağılmış boyaların fırçalama direncini arttırmakla kalmaz, aynı zamanda aşırı yüklü dağınık boyaların fırçalama direncini arttırır.
NX 795 TM ester alkol, lateks boyaları için önde gelen birleşim maddesidir. Çeşitli hava koşullarında ve farklı porozite seviyelerine sahip yüzeylerde, lateks boyaların her çeşidinde iyi performans gösterir. NX 795 TM ester alkol, düşük seviyeli kaynaştırmada en yüksek film bütünlüğü seviyesini sağlar ve boyanın performans özelliklerini arttırır Rötuş direnci, yıkanabilirlik, renk gelişimi, termal esneklik ve çamur çatlamasına direnç dahil olmak üzere, Eastman NX 795 TM; Ester alkol, birleştirici koyulaştırıcılarla kullanıldığında kalınlaşma verimliliğini de arttırır.
NX 795 TM ester alkol aynı zamanda diğer çeşitli uygulamalarda iyi çalışır. Bobin kaplamaları ve yüksek fırında emaye kullanmak için bir geciktirici çözücü olarak ideal bir seçimdir. Eşsiz denge özellikleri, cevher flotasyonu / köpürmesi, petrol sondajı çamurları, ahşap koruyucu taşıyıcılar ve zemin cilaları gibi çeşitli kimyasal özel uygulamalar için de yararlı olmaktadır. Tampon çözücü olarak tırnak cilasında da kullanılabilir.

 

 


TEKANOLUN TEMEL FİZİKSEL VE ​​KİMYASAL ÖZELLİKLERİ İLE İLGİLİ BİLGİ

 

 

Moleküler Formül: C12H24O3
Moleküler Ağırlık: 216.32
Fiziksel Durum: Sıvı
Renk: Renksiz
Koku: Hafif
Erime noktası: -50C
Kaynama noktası: 244C
Durum: Sıvı
Parlama noktası: 120C (o-fincan)
Flamable Limit: 149C'de% 0,62 - 201C'de% 4,24
Yoğunluk: 20C'de 0.95
Buhar Basıncı: 20 ° C'de 0.013 mbar (0.010 mmHg)
Çözünürlük
@ 20 ° C'de:% 0.1
@ 20 ° C su:% 3.0
Özgül Ağırlık @ 20 ° C / 20 ° C'de: 0.95
Yüzey Gerilimi @ 20 ° C'de: 28.9 din / cm
Buhar Yoğunluğu (hava = 1) 7.5
Buhar basıncı
@ 20 ° C 0.0013 KPa (0.01 mm Hg)
@ 25 ° C 0.00173 KPa
@ 55 ° C 0.033 KPa
Wt / Vol @ 20 ° C 0,95 kg / L (7,9 lb / gal)
@ 20 ° C'de Sıvı Viskozite: 13.5 cP (mPa.s)
Nitro Selüloz Çözünürlüğü: Aktif
Bölme katsayısı (n-oktanol / su): log pw: 2.34 - 3.2
Suda Çözünürlük: 18-22C'de 858 mg / L *
Katkı Maddeleri: Katkı maddesi tipik olarak mevcut değildir.
Kendiliğinden tutuşma Sıcaklığı: 388 ° C (ASTM E659)
Ayrışma Sıcaklığı: Veri mevcut değil.
Dinamik Viskozite: 12.9 mPa.s (25 ° C)
Kinematik viskozite: 13.6 mm2 / s (25 ° C)
Safsızlıklar: 2,2,4-Trimetil pentan-l, 3-diol% 0.1 (CAS RN: 144-19-4); TXBI
(NX 795 izobütirat)% 0.6 (CAS RN = 6846-50-0); NPGDI% 0.1; TMPI
: Iz; 3-izobütiroksi-2,2,4-trimetil pentanol: iz;
3-okso-2,2,4-trimetil penten-1-ol: iz; Keto ester: iz.

 

 


NX 795 UYGULAMA / KULLANIMI

 

 

NX 795 alkol esterinin özelliklerinin eşsiz dengesi, çeşitli
Diğer başvurulardan:
= Mimari, endüstriyel ve bakım pazarlarında lateks kaplamalar için kaynaşmış
= Bobin kaplamalarında ve yüksek fırında emaye kullanılan geciktirici çözücü
= Plastikleştiriciler, vb. Için ester türevlerinin sentezi için kimyasal ara madde
= Zemin cilaları için kaynaştırıcı
= Solventli kaplamalar için geciktirici çözücü
= Ahşap koruyucu taşıyıcılar
= Zemin cilaları
Litografik ve letterpress yağlı mürekkeplerde "tatlandırıcı" çözücü
= Elektro çökeltme primerleri / kaplamaları için kaynaştırıcı
= Sondaj çamurlarında ve cevher flotasyon süreçlerinde geri kazanım solventi
= Bu ürün, ideal bir su bazlı kaynaştırma ajanıdır ve bir film tabakası üzerinde iyi bir film oluşturucu etkiye sahiptir.
Çeşitli emülsiyon polimer sistemleri ve minimum film oluşturucu sıcaklığı düşürebilir.
Filmlerin oluşturulması zor olan durumlarda (örneğin yüksek cam geçiş sıcaklığı,
Düşük inşaat ortam sıcaklığı) ve son derece çeşitli
Emülsiyonlar, lateks boyalar ve sentezlenen yapışkanlar gibi su bazlı kaplama sistemleri
Metakrilat ve vinil asetat.
= Endüstriyel Bakım ve Denizcilik
= Grafik Sanatlar - Baskı Mürekkepleri (Litografik Baskı ve Yağ Baskısı Yağlı Mürekkepler)
= Petrol Sahası Kimyasalları - Sondaj Çamurları / Çakıl Ajan / Cevher Flotasyonu
= Reaktif Ara Madde - Plastifiyanlar İçin Ester Türevleri

 

 


NX 795 DEPOLAMA

 

Isı, kıvılcım ve alevden uzak tutun. Tutuşma kaynaklarından uzak tutun. Sıkıca kapalı bir kapta saklayın. Uyumsuz maddelerden uzakta serin, kuru ve iyi havalandırılmış bir yerde saklayın. Peroksit seviyelerini% 1'in altında tutmak için inhibitör düzeylerini düzenli olarak kontrol edin. Açıldıktan sonra tekrar kapatılamadan önce az miktarda konteyneri temizleyin.

 

 


NX 795

 

 

NX 795 coalescing agent for latex products
Promotes uniform film formation with optimal properties
Universal in all latex systems
Easy to incorporate
Reduces minimum film-formation temperature
Non-VOC and non-HAP provides cleaner air and safer handling

 

 

Superior properties
NX 795 is an effective coalescing agent for latex formulations
such as acrylic dispersions, styrene acrylics and vinyl acetate
co-polymer dispersions. This ester alcohol effectively reduces the
minimum film-formation temperature (MFFT), and provides
further benefits in end-product properties including higher
coating gloss, increased film integrity, reduced film porosity
and less cracking.
Universal
Incorporation of NX 795 results in optimal paint performance
even at lower drying temperatures. NX 795 also facilitates the
use of hard latexes at low temperatures, broadening the range
of practical application temperatures in many latex paint
formulations. NX 795 does not dissolve in water, but is readily
absorbed by latex particles making it an effective film-forming
additive even when applying paint on porous substrates and in
moist environments.
NX 795 properties and performance
The following semi-gloss acrylic paint formulation
demonstrates the effect of NX 795 on the finished
product:
OH O
O
Isomeric mixture of 2,2,4-Trimethylpentane-1,3-diol monoisobutyrates
CAS no. 25265-77-4
EINECS no. 246-771-9
The semi-gloss acrylic paint formulation
No. Component Weight %
1 Glycol 2.56 0
pigment grind
2 Water 3.42 0
3 Amine 0.21 0
4 Dispersing agent 1 0.21 0
5 Dispersing agent 2 0.32 0
6 Levelling aid 0.43 0
7 Pigment grinding vehicle 3.32 0
8 White TiO2
pigment 24.81 0
9 Acrylic co-polymer dispersion 62.79 0
let-down
10 Silicone defoamer 0.86 0
11 Associative thickener 1.07 0
TOTAL 100.00 0
Solid Content ca. 55%, Viscosity ca. 10,000 mPas, Gloss 60° ca. 50
Enhancing latex products
Typical properties
Density 0.947 kg/dm3
Solubility at 20°C
- in water (insoluble)
- water in NX 795 max 0.10 weight%
Evaporation rate 0.002 (BuAc = 1)
Refractive index at 20°C 1.4423
Vapor pressure 293.15 K (20°C) <0.01 kPa
Boiling point at 101.3 kPa 254°C
Freezing point -50°C
Reducing MFFT
NX 795 is an extremely effective additive for decreasing
the minimum film-formation temperature of latex paints.
A substantial reduction in MFFT can be achieved by adding
small amounts of NX 795 to paint. In most cases a suitable
addition level is 5-10%, based on latex solids. The harder the
polymer, the higher the level needed; possibly up to 20% for
polymer solids.
Ensuring the optimal performance of a latex paint requires
just the right amount of coalescing aid. The MFFT of the latex
dispersions and the efficiency of the coalescing aid to decrease
the MFFT are important in determining the correct amount
of NX 795 to add. One should also take into account the
conditions under which the paint is applied. The MFFT for
indoor applications is generally 0°C to 5°C, but the MFFT
for outdoor applications is often considerably lower.
Improving hardness
NX 795 contributes to good hardness development in paint
film at normal levels of addition. Excessive amounts of coalescent should be avoided as this will lead to retarded hardness
development.
30
20
10
0
0 2 1 3 4
% NX 795 of the total formulation
MFFT, °C
40
35
30
25
0
0 5 10 15 20 25 30
Time, days
König pendulum, s
The effect of NX 795
on film-formation temperature
Hardness development during drying of an acrylic latex paint formulation containing 3% NX 795
Effective additives for ideal properties
Proven pH & viscosity stability
Essential requirements for any high-quality paint product are pH and viscosity stability. Hydrolysis of the coalescing agent would reduce paint performance but an experiment demonstrates the stability of NX 795. NX 795 is a hydrolytically
stable coalescing aid that is hardly affected by the alkaline nature of typical latex formulations. Extremely high pH values(>10) are however not recommended.
In a stable paint, the paint viscosity is expected to remain virtually constant over the time of storage. In this test, paint samples were stored at 23°C and 50°C. Viscosity was measured at specified intervals by a Brookfield low shear viscometer.
Negligible change of the paint viscosity is a good indication of the hydrolytic resistance of NX 795 coalescing agent.
Safer performance with environmentally friendly paint
Thanks to its properties, only very low concentrations of NX 795 are emitted during the use of paints containing NX 795 as the coalescing agent. NX 795 is not classified as VOC material in
Europe (1999/13/EC and 2004/42/CE) and not as HAP in the U.S. (Clean Air Act 1990). NX 795 is not classified as a VOC per China State Environmental Protection Agency. The high boiling point, >250°C, and low vapor pressure, <0.01 kPa at 20°C, indicate low volatility of the NX 795 coalescing aid.
Ensuring Optimal Results
NX 795 can be easily incorporated into a paint formulation
during the last stages of paint manufacture. Once the coalescent is added it is recommended to allow the paint to stabilize
overnight prior to application or testing

 

 

NX 795
? 2,2,4-Trimethyl-1,3-pentanediol-monoisobutyrate
? Clear colourless liquid
? Classified agent as non-VOC according to European classification (1999/13/EC and 2004/42/EC)

 

 

Property Value Unit Method1
Purity of NX 795 min. 99 % PO 130-2
Acid number of NX 795 max. 0.5* mg KOH/g PO 110-10
Colour of NX 795 max. 10 Hazen PO 105-4
Water content of NX 795 max. 0.1 % PO 109-10
Boiling point of NX 795 255 °C
Density of NX 795 (20 °C) 947 Kg/m³
Freezing point of NX 795 -50 °C
Vapour pressure of NX 795 (20 °C) <0.01 kPa
*corresponds to max. 0,08 % isobutyric acid or max. 0,05 % acetic acid
1 internal method based upon the specified norm
Application Advice & Processing
? Coalescing agent in Latex paints formulations
? Intermediates for plasticizers
Product Safety of NX 795
Before handling, please read the Safety Data Sheet of this product for advice on safety, use and disposaL

 

 

NX 795 is a clear, colorless liquid ester alcohol used as a coalescing agent for aqueous dispersions. 
NX 795 is used in decorative and industrial coatings.

 

 

NX 795 (TRIMETHYL PENTANEDIOLE MONOISOBUTYRATE) : PRODUCT INFORMATION PAGE 
nx-795 (trimethyl pentanediole monoisobutyrate) 25265-77-4 246-771-9 Synthomer Speciality Additives small bulk, 28.5 Kg, 195 Kg, 950 Kg

 

GENERAL DESCRIPTION of NX 795

 

Due to low vapor pressure, it meets VOC limitations according to many standards. Burning and poisoning are low, and there is high fragmentation in the environment. A large proportion of water-based paints (Latex Paints) require coalescence additives to form a film at room temperature. In others, these contributions play a role in the film formation, ensuring film integrity and in extreme conditions outside room temperature.
NX 795 is the highest performance additive that can be used for these purposes even at low concentrations. NX 795 is a very odorous liquid, with little effect on the odor of paint in many stages of drying. It not only increases the scrubbing resistance of normal disperse dyes but also increases the scrubbing resistance of over-charged disperse dyes.
NX 795TM ester alcohol is the premier coalescent for latex paints. It performs well in all types of latex paints, in a variety of weather conditions, and over substrates with different levels of porosity.NX 795TM ester alcohol provides the highest level of film integrity at low levels of coalescent, enhancing the performance properties of the paint including low temperature coalescence, touch-up, scrub resistance, washability, color development, thermal flexibility, and resistance to mudcracking. Eastman NX 795TM; ester alcohol also enhances thickening efficiency when used with associative thickeners. 
NX 795TM ester alcohol also works well in a variety of other applications. It is an ideal choice as a retarder solvent for use in coil coatings and high-bake enamels. Its unique balance of properties also makes it useful for a variety of chemical specialty applications such as ore flotation / frothing, oil-drilling muds, wood preservative carriers, and floor polishes.NX 795 can also be used as a solvent in nail polish.

 

 


INFORMATION on BASIC PHYSICAL and CHEMICAL PROPERTIES of NX 795

 

 

Molecular Formula : C12H24O3
Molecular Weight : 216.32
Physical State: Liquid
Colour : Colourless
Odour : Mild
Melting Point : -50C
Boiling Point : 244C
State : Liquid
Flash Point : 120C (o-cup)
Flamable Limit : 0.62% at 149C - 4.24% at 201C
Density : 0.95 at 20C
Vapour Pressure : 0.013 mbar (0.010 mmHg) at 20C
Solubility
in Water, @ 20°C: 0.1%
Water in, @ 20°C:3.0%
Specific Gravity @ 20°C/20°C: 0.95
Surface Tension @ 20°C: 28.9 dynes/cm
Vapor Density (air = 1) 7.5
Vapor Pressure
@ 20°C 0.0013 KPa (0.01 mm Hg)
@ 25°C 0.00173 KPa
@ 55°C 0.033 KPa
Wt/Vol @ 20°C 0.95 kg/L (7.9 lb/gal)
Liquid Viscosity @ 20°C: 13.5 cP (mPa·s)
Nitrocellulose Solubility: Active
Partition coefficient (n-octanol/water): log Pow: 2.34 - 3.2
Water Solubility : 858 mg/L at 18-22C *
Additives : No additive typically present.
Autoignition Temperature: 388 °C (ASTM E659)
Decomposition Temperature: No data available.
Dynamic Viscosity: 12.9 mPa.s (25 °C)
Kinematic viscosity: 13.6 mm2/s (25 °C)
Impurities : 2,2,4-Trimethyl pentane-1,3-diol 0.1% (CAS RN: 144-19-4); TXBI
(NX 795 isobutyrate) 0.6% (CAS RN = 6846-50-0); NPGDI 0.1%; TMPI
: trace; 3-isobutyroxy-2,2,4-trimethyl pentanol: trace;
3-oxo-2,2,4-trimethyl penten-1-ol: trace; keto ester: trace.

 

 


APPLICATION/USES of NX 795

 

 

The unique balance of properties in NX 795 alcohol ester also makes it useful for a variety
of other applications:
= Coalescent for latex coatings in the architectural, industrial, and maintenance markets
= Retarder solvent for use in coil coatings and high-bake enamels
= Chemical intermediate for synthesis of ester derivatives for plasticizers, etc.
= Coalescent for floor polishes
= Retarder solvent for solventborne coatings
= Wood preservative carriers
= Floor polishes
= "Sweetener" solvent in lithographic and letterpress oil-based inks
= Coalescent for electro deposition primers/coatings
= Recovery solvent in drilling muds and ore flotation processes
= This product is an ideal water-based coalescent agent, and has preferable film-forming effect to a
various kind of emulsion polymer systems and could reduce minimum film forming temperature.
nx 795 can be applied in situations that are difficult to form films (e.g. high glass transition temperature,
low construction environment temperature ), and is extremely appropriate for various kinds of
water-based coating systems such as emulsions, latex paints and adhesives synthesized from
methacrylate, and vinyl acetate.
= Industrial Maintenance and Marine
= Graphic Arts - Printing Inks (Lithographic and Letterpress oil-based inks)
= Oil Field Chemical - Drilling Muds/Frothing Agent/Ore Flotation
= Reactive Intermediate - Ester Derivatives for Plasticizers

 

 


STORAGE of NX 795

 

Keep away from heat, sparks, and flame. Keep away from sources of ignition. Store in a tightly closed container. Store in a cool, dry, well-ventilated area away from incompatible substances. Regularly check inhibitor levels to maintain peroxide levels below 1%. After opening, purge container with nitrogen before reclosing. Periodically test for peroxide formation on long-term storage. Addition of water or appropriate reducing materials will lessen peroxide formation.

 

NX 795

 

Agent de coalescence NX 795 pour produits en latex
Favorise la formation d'un film uniforme avec des propriétés optimales
Universel dans tous les systèmes en latex
Facile à intégrer
Réduit la température minimale de formation de film
Sans COV et sans HAP pour un air plus pur et une manipulation plus sûre

 

 

Propriétés supérieures
NX 795 est un agent coalescent efficace pour les formulations de latex
comme les dispersions acryliques, les acryliques styréniques et l'acétate de vinyle
dispersions de copolymères. Cet alcool ester réduit efficacement la
température minimale de formation de film (MFFT), et fournit
avantages supplémentaires dans les propriétés du produit final,
brillant du revêtement, intégrité accrue du film, porosité du film réduite
et moins de fissures.
Universel
L'incorporation de NX 795 donne des performances de peinture optimales
même à des températures de séchage plus basses. NX 795 facilite également la
utilisation de latex durs à basse température, élargissant la gamme
des températures d'application pratiques dans de nombreuses peintures au latex
Formulations. Le NX 795 ne se dissout pas dans l'eau, mais est facilement
absorbé par les particules de latex, ce qui en fait un filmogène efficace
additif même lors de l'application de peinture sur des substrats poreux et
environnements humides.
Propriétés et performances du NX 795
La formulation de peinture acrylique semi-brillante suivante
démontre l'effet du NX 795 sur le fini
produit:
OH O
IL
Mélange isomère de monoisobutyrates de 2,2,4-triméthylpentane-1,3-diol
N ° CAS. 25265-77-4
EINECS no. 246-771-9
La formulation de peinture acrylique semi-brillante
Non. % De poids des composants
1 Glycol 2,56 0
broyage de pigment
2 Eau 3,42 0
3 amine 0,21 0
4 Agent dispersant 1 0,21 0
5 Agent dispersant 2 0,32 0
6 Aide au nivellement 0,43 0
7 Véhicule de broyage de pigments 3,32 0
8 TiO2 blanc
pigment 24,81 0
9 Dispersion de copolymère acrylique 62,79 0
Penmarlam
10 Antimousse silicone 0,86 0
11 Épaississant associatif 1,07 0
TOTAL 100,00 0
Contenu solide env. 55%, viscosité env. 10000 mPas, brillant 60 ° ca. 50
Amélioration des produits en latex
Propriétés typiques
Densité 0,947 kg / dm3
Solubilité à 20 ° C
- dans l'eau (insoluble)
- eau dans NX 795 max 0,10% en poids
Taux d'évaporation 0,002 (BuAc = 1)
Indice de réfraction à 20 ° C 1,4423
Pression de vapeur 293,15 K (20 ° C) <0,01 kPa
Point d'ébullition à 101,3 kPa 254 ° C
Point de congélation -50 ° C
Réduire le MFFT
Le NX 795 est un additif extrêmement efficace pour diminuer
la température minimale de formation de film des peintures au latex.
Une réduction substantielle du MFFT peut être obtenue en ajoutant
de petites quantités de NX 795 à peindre. Dans la plupart des cas, un
le niveau d'addition est de 5 à 10%, basé sur les solides en latex. Plus le
polymère, plus le niveau requis est élevé; jusqu'à 20% pour
solides polymères.
Assurer les performances optimales d'une peinture au latex nécessite
juste la bonne quantité d'aide coalescente. Le MFFT du latex
les dispersions et l'efficacité de l'aide à la coalescence pour diminuer
les MFFT sont importants pour déterminer le montant correct
de NX 795 à ajouter. Il faut également tenir compte des
conditions dans lesquelles la peinture est appliquée. Le MFFT pour
les applications intérieures sont généralement de 0 ° C à 5 ° C, mais le MFFT
pour les applications extérieures est souvent considérablement plus faible.
Amélioration de la dureté
Le NX 795 contribue au bon développement de la dureté de la peinture
film à des niveaux d'addition normaux. Des quantités excessives de coalescence doivent être évitées car cela entraînerait un retard de dureté
développement.
30
20
dix
0
0 2 1 3 4
% NX 795 de la formulation totale
MFFT, ° C
40
35
30
25
0
0 5 10 15 20 25 30
Temps, jours
Pendule de König, s
L'effet du NX 795
sur la température de formation du film
Développement de la dureté lors du séchage d'une formulation de peinture acrylique au latex contenant 3% de NX 795
Additifs efficaces pour des propriétés idéales
Stabilité éprouvée du pH et de la viscosité
Les exigences essentielles pour tout produit de peinture de haute qualité sont la stabilité du pH et de la viscosité. L'hydrolyse de l'agent coalescent réduirait les performances de la peinture mais une expérience démontre la stabilité du NX 795. Le NX 795 est un
aide à la coalescence stable qui n'est guère affectée par la nature alcaline des formulations de latex typiques. Des pH extrêmement élevés (> 10) ne sont cependant pas recommandés.
Dans une peinture stable, la viscosité de la peinture devrait rester pratiquement constante pendant la durée de stockage. Dans ce test, les échantillons de peinture ont été stockés à 23 ° C et 50 ° C. La viscosité a été mesurée à des intervalles spécifiés par un viscosimètre Brookfield à faible cisaillement.
Un changement négligeable de la viscosité de la peinture est une bonne indication de la résistance hydrolytique de l'agent coalescent NX 795.
Des performances plus sûres avec une peinture écologique
Grâce à ses propriétés, seules de très faibles concentrations de NX 795 sont émises lors de l'utilisation de peintures contenant du NX 795 comme agent coalescent. Le NX 795 n'est pas classé comme matériau COV dans
Europe (1999/13 / CE et 2004/42 / CE) et non comme HAP aux États-Unis (Clean Air Act 1990). Le NX 795 n'est pas classé comme COV par l'Agence chinoise de protection de l'environnement. Le point d'ébullition élevé,> 250 ° C, et la basse pression de vapeur, <0,01 kPa à 20 ° C, indiquent une faible volatilité de l'aide de coalescence NX 795.
Assurer des résultats optimaux
NX 795 peut être facilement incorporé dans une formulation de peinture
pendant les dernières étapes de la fabrication de peinture ré. Une fois le coalescent ajouté, il est recommandé de laisser la peinture se stabiliser
pendant la nuit avant l'application ou le test

 

 

NX 795
? 2,2,4-triméthyl-1,3-pentanediol-monoisobutyrate A
? Liquide incolore clair
? Agent classé comme non-COV selon la classification européenne (1999/13 / EC et 2004/42 / EC)

 

 

Méthode de la valeur unitaire de la propriété1
Pureté de NX 795 min. 99% PO 130-2
Nombre d'acide de NX 795 max. 0,5 * mg KOH / g PO 110-10
Couleur du NX 795 max. 10 Hazen PO 105-4
Teneur en eau de NX 795 max. 0,1% PO 109-10
Point d'ébullition de NX 795 255 ° C
Densité de NX 795 (20 ° C) 947 Kg / m³
Point de congélation de NX 795 -50 ° C
Pression de vapeur de NX 795 (20 ° C) <0,01 kPa
* correspond à max. 0,08% d'acide isobutyrique ou max. 0,05% d'acide acétique
1 méthode interne basée sur la norme spécifiée
Conseils et traitement des demandes
? Agent de coalescence dans les formulations de peintures au latex
? Intermédiaires pour plastifiants
Sécurité du produit du NX 795
Avant la manipulation, veuillez lire la fiche de données de sécurité de ce produit pour des conseils sur la sécurité, l'utilisation et l'élimination

 

 

Le NX 795 est un alcool ester liquide clair et incolore utilisé comme agent de coalescence pour les dispersions aqueuses.
Le NX 795 est utilisé dans les revêtements décoratifs et industriels.

 

 

NX 795 (MONOISOBUTYRATE DE PENTANEDIOLE TRIMÉTHYLIQUE): PAGE D'INFORMATION SUR LE PRODUIT
nx 795 (monoisobutyrate de triméthyl pentanediole) 25265-77-4 246-771-9 Additifs de spécialité Synthomer petit volume, 28,5 Kg, 195 Kg, 950 Kg

 

Acar Kimya A.Ş. © 2015 Tüm Hakları Saklıdır.