ESCOREZ 2203 LC

SYNONYMS
Escorez 2203; ESCOREZ 2203; ESKOREZ 2203; eskorez 2203; EZKORES 2203; EZKOREZ 2203; (Americas; Escorez 1304 (AM & EU; Escorez 1310LC ; Escorez 1315 (Americas); Escorez 2203LC (AM & EU); Escorez 5300; Escorez 5320; EscorezTM 534; EscorezTM 538; EscorezTM 5400; EscorezTM 5415; EscorezTM 5600; EscorezTM 5615; EscorezTM 5637; EscorezTM 5690; Hydrocarbon Resins (Escorez); Hydrocarbon Resins (Escorez); Escorez; Escorez 1102; Escorez 1102 ; Escorez 1304 ; Escorez 1310 LC; Escorez 1401 ; Escorez 2101 ; Escorez 2173 ; Escorez 2184 ; Escorez 2203; Escorez 2520 ; Escorez 5300 ; Escorez 5320 ; Escorez 5380 ; Escorez 5400 ;Escorez 5415;Escorez 5490; Escorez 5600; Escorez 5615 ; Escorez 5690 
EscorezTM 1304 (AM & EU; EscorezTM 1310LC ; EscorezTM 1315 (Americas); EscorezTM 2203LC (AM & EU); EscorezTM 5300; EscorezTM 5320; EscorezTM 534; EscorezTM 538; EscorezTM 5400; EscorezTM 5415; EscorezTM 5600; EscorezTM 5615; EscorezTM 5637; EscorezTM 5690; Hydrocarbon Resins (Escorez); Hydrocarbon Resins (Escorez); Escorez; Escorez 1102; Escorez 1102 ; Escorez 1304 ; Escorez 1310 LC; Escorez 1401 ; Escorez 2101 ; Escorez 2173 ; Escorez 2184 ; Escorez 2203; Escorez 2520 ; Escorez 5300 ; Escorez 5320 ; Escorez 5380 ; Escorez 5400 ;Escorez 5415;Escorez 5490; Escorez 5600; Escorez 5615 ; Escorez 5690

 

Escorez 2203 LC
Escorez hydrocarbon resins are amorphous, glassy, low molecular weight hydrocarbon polymers. They have tailored molecular weight distributions designed to fit specific application requirements.
Product Description: EscorezTM 2203LC is a premium aromatic modified aliphatic hydrocarbon resin with a narrow molecular weight distribution. It is characterized by low color and low volatility. It is primarily designed for tackification of styrene-isoprene-styrene (SIS) block copolymers, but also useful as tackifiers for natural rubber, metallocene polyolefins, Butyl rubber, EVA, APP and APAO.
Availability: Africa & Middle East, Central America, Europe, North America and South America.EscorezTM 2203LC (AM & EU) Tackifying Resin
Escorez 2203LC (AM & EU) Tackifying Resin.

 

 

Escorez 2203LC (AM & EU)
Tackifying Resin

 

 

EscorezTM 2203LC is a premium aromatic modified aliphatic hydrocarbon resin with a narrow molecular weight distribution. It is characterized by low color and low volatility. It is primarily designed for tackification of styrene-isoprene-styrene (SIS) block copolymers, but also useful as tackifier for natural rubber, metallocene polyolefins, Butyl rubber, EVA, APP and APAO.

Properties Minimum Maximum Unit Test Method
Softening Point 89.0 96.0 °C ETM 22-24
Color - Initial -- 40 YI ETM 22-13
Wax Cloud Point (30/45/25) -- 105 °C ETM 22-10

 

EscorezTM 2203LC (AM & EU) Tackifying Resin the interlocking "X" device and other product or service names used herein are trademarks of ExxonMobil, unless indicated otherwise. This document may not be distributed, displayed, copied or altered without l's prior wriEscorezTM 2203LC (AM & EU) Tackifying Resintten authorization. To the exten EscorezTM 2203LC (AM & EU) Tackifying Resint authorizes distributing, displaying and/or copying of this document, the user may do so only if the document is unaltered and complete, including all of its headers, footers, disclaimers and other information. You may not copy this document to or reproduce it in whole or in part on a website. ExxonMobil does not guarantee the typical (or other) values. Any data included herein is based upon analysis of representative samples and not the actual product shipped. The information in this document relates only to the named product or materials when not in combination with any other product or materials. We based the information on data believed to be reliable on the date compiled, but we do not represent, warrant, or otherwise guarantee, expressly or impliedly, the merchantability, fitness for a particular purpose, freedom from patent infringement, suitability, accuracy, reliability, or completeness of this information or the products, materials or processes described. The user is solely responsible for all determinations regarding any use of material or product and any process in its territories of interest. We expressly disclaim liability for any loss, damage or injury directly or indirectly suffered or incurred as a result of or related to anyone using or relying on any of the information in this document. This document is not an endorsement of any nol product or process, and we expressly disclaim any contrary implication. The terms "we," "our," " stewarded.

 

 

Information provided EscorezTM 2203LC (AM & EU) Tackifying Resin
Softening Pt., °C 92
Color, %50 in Toluen, Yl 24
Tg, °C 48
Molecular Weight, Mn, g/mol 1120
Molecular Weight, Mw, g/mol 1930
EscorezTM 2203LC (AM & EU) Tackifying Resin
Hydrocarbon Resins (Escorez)

 

 

Hydrocarbon Resins (Escorez)
Color, %50 in Toluen, Yl Molecular Weight, Mn, g/mol Molecular Weight, Mw, g/mol Softening Pt., °C Tg, °C
Escorez 1102 39 1270 2690 100 51
Escorez 1102 F 30 1490 4920 101 51
Escorez 1102 RM 38 1250 3060 98 50
Escorez 1304 32 1250 2150 100 55
Escorez 1310 LC 29 1090 1680 94 49
Escorez 1401 31 1130 2110 118 74
Escorez 2101 78 870 1920 92 44
Escorez 2173 75 810 1470 89 45
Escorez 2184 83 870 1850 98 47
Escorez 2203 LC 24 1120 1930 92 48
Escorez 2520 16 320 430 20 -15
Escorez 5300 <0,5 290 520 106 56
Escorez 5320 <0,5 360 670 126 72
Escorez 5340 <0,5 400 680 139 89
Escorez 5380 <0,5 260 500 86 89
Escorez 5400 <1,5 290 550 103,5 52
Escorez 5415 <1,5 330 640 119 69
Escorez 5490 <1,5 270 540 91 38
Escorez 5600 <2 540 730 103 56
Escorez 5615 <2 490 800 118 68
Escorez 5690 <2 340 670 90,5 44

 

 

The Inventive Resin was also compared with some 5 competitive resin samples. Tested were Escorez 1310 LC, an aliphatic resin like Piccotac 95E, and Escorez 2203 LC, a slightly aromatic modified resin comparable to Hercotac 1148.
Further Hercules RESIN A was compared as well.
10 Hercules RESIN A is like Hercules RESIN B a more aromatic modified resin than Escorez 2203 and Hercotac 1148 .

 

 

~ 34 1) 2 1 9 9 3 3 1 Table 8. h'M PSA T:erformance in Kraton D 1107 Ex. No. 6a 6b 6c 6d Kraton D 1107 100 100 100 100 lNV~;hllV~: RESIN 120 5 Escorez 2203 LC 120 ,Escorez 2203 LC 120 Shellflex 451 FC 20 20 20 20 I rganox 1010 2 2 2 2 10 Viscosity at 175-C 37900 85400 45000 40000 ( mPas ~
sall tack (cm) 3 . 0 2 . 6 3 . 8 6 . 6 PEEL to STEEL 20.7 14.5 17.8 18.1 (N/25mm) 15 LOOP tack (N/25 mm) 32.8 19.1 30.7 25.7 SAFT (0.5 kg, C) 93 102 95 85 Shear to carton 232 337 242 383 (40 C, 1 kg,min) Shear to steel 120 73 134 177 20 (40 C,2.5 kg,min) Shear to steel 809 1446 781 102 (70 C,0.5 kg,min) The results clearly show again that the melt viscosity and the rolling ball tack using the Inventive 25 Resin are comparable to a slightly aromatic modified resin like Escorez 2203 LC. The rolling ball tack using Hercules RESIN A was found to be higher due to the higher molecular weight. The hot melt viscosity using Escorez 1310 LC is higher than observed for Piccotac 95E
and especially the Inventive Resin. The shear to steel at 70 C using the Inventive Resin was found to be better than for the Hercules RESIN A. The use of Escorez 2203 LC gives a better high temperature shear to steel like 5 found for Piccotac 95E but also gives the highest viscosity .Escorez 1310 LC - A petroleum resin available from Exxon containing about 0.3% by weight of polymerized 5 styrene and having a softening point of about 93.5 C.

 

 

Escorez 2203 LC - A petroleum resin available A;n;n~ about 8 to 10 wt% of polymerized styrene and having a softening point of about 92 C and a number average molecular weight of about 1150.
Winqtack 95 - A petroleum resin available from Good Year like Piccotac 95E and Escorez 1310 having a softening point of about 96 C and a number average molecular weight of about 1100.
Hercules RESIN A hYdrocarbon resin - A petroleum 15 resin available from Hercules containing about 10 to 25 wt% of some polymerized aromatic monomers and having a softening point of about 95 C.

 

 


Escorez 2203 LC
Escorez hidrokarbon reçineleri, şekilsiz, camsı, düşük moleküler ağırlıklı hidrokarbon polimerleridir. Özel uygulama gereksinimlerine uyacak şekilde tasarlanmış moleküler ağırlık dağılımlarına sahiptirler.
Ürün Açıklaması: Escorez TM 2203LC, dar bir moleküler ağırlık dağılımına sahip birinci sınıf bir aromatik modifiye alifatik hidrokarbon reçinesidir. Düşük renk ve düşük uçuculuk ile karakterizedir. Öncelikle stiren-izopren-stiren (SIS) blok kopolimerlerinin yapışkanlaştırılması için tasarlanmıştır, ancak aynı zamanda doğal kauçuk, metalosen poliolefinler, Butil kauçuğu, EVA, APP ve APAO için yapışkanlaştırıcılar olarak da faydalıdır.
Kullanılabilirlik: Afrika ve Orta Doğu, Orta Amerika, Avrupa, Kuzey Amerika ve Güney Amerika.Escorez TM 2203LC (AM ve AB) Tackifying Resin
Escorez 2203LC (AM ve AB) Yapışkanlaştırıcı Reçine.

 

 

Escorez 2203LC (AM ve AB)
Yapışkan Reçine

 

Escorez TM 2203LC, dar bir molekül ağırlığı dağılımına sahip birinci sınıf bir aromatik modifiye alifatik hidrokarbon reçinesidir. Düşük renk ve düşük uçuculuk ile karakterizedir. Öncelikle stiren-izopren-stiren (SIS) blok kopolimerlerinin yapışkanlaştırılması için tasarlanmıştır, fakat aynı zamanda doğal kauçuk, metalosen poliolefinler, Butil kauçuğu, EVA, APP ve APAO için yapışkanlaştırıcı olarak da faydalıdır.

 

Asgari Maksimum Birim Test Yöntemi
Yumuşama Noktası 89.0 96.0 ° C ETM 22-24
Renk - İlk - 40 YI ETM 22-13
Balmumu Bulut Noktası (30/45/25) - 105 ° C ETM 22-10

 

Escorez TM 2203LC (AM ve AB) Yapıştırıcı Reçine Birbirine kenetlenen "X" cihazı ve burada kullanılan diğer ürün veya hizmet adları Reçine, aksi belirtilmediği sürece ExxonMobil'in ticari markalarıdır. Bu belge önceden wriEscorez TM 2203LC (AM & EU) Tackifying Resintten izni olmadan dağıtılamaz, gösterilemez, kopyalanamaz veya değiştirilemez. Eski Escorez TM 2203LC'ye (AM & AB) Tackifying Resint, bu belgenin dağıtılması, gösterilmesi ve / veya kopyalanmasına izin verir, kullanıcı bunu yalnızca tüm başlıkları, altbilgileri, feragatnameleri ve diğer belgeleri de dahil olmak üzere, belge değiştirilmemiş ve tamamlanmışsa yapabilir bilgi. Bu belgeyi bir web sitesinde tamamen veya kısmen kopyalayamaz veya çoğaltamazsınız. ExxonMobil, tipik (veya diğer) değerleri garanti etmez. Buraya dahil edilen herhangi bir veri, gönderilen gerçek ürünü değil temsili örneklerin analizine dayanmaktadır. Bu belgedeki bilgiler, yalnızca başka bir ürün veya malzeme ile birlikte olmadığında adlandırılmış ürün veya malzemelerle ilgilidir. Bilgiyi, derlendiği tarihte güvenilir olduğuna inanılan verilere dayandırırız; ancak satılabilirliği, belirli bir amaca uygunluğu, patent ihlali özgürlüğünü, uygunluğunu, doğruluğunu, güvenilirliğini temsil etmemekte, garanti etmemekte veya başka şekilde garanti etmemekteyiz. veya bu bilgilerin veya açıklanan ürünlerin, malzemelerin veya işlemlerin eksiksizliği. Kullanıcı, herhangi bir malzemenin veya ürünün kullanımıyla ve ilgilendiği bölgelerdeki herhangi bir işlemle ilgili tüm tespitlerden tek başına sorumludur. Bu belgedeki herhangi bir bilgiyi kullanan veya kullanan herhangi birisinin sonucu olarak veya dolaylı olarak doğrudan veya dolaylı olarak zarar gören veya bununla ilgili herhangi bir kayıp, hasar veya yaralanma için sorumluluk kabul etmiyoruz. Bu belge herhangi bir nol ürün ya da sürecinin onaylanması değildir ve açıkça herhangi bir çelişki reddedilir.

Acar Kimya A.Ş. © 2015 Tüm Hakları Saklıdır.